Reinforced Sheet-GSS

GSS is manufactured from Flexible Graphite Foil bonded to a 0.002" (0.05mm) thick GLUED SUS316 or SUS304 stainless steel sheet insert. The product is recommended to use in pumps, fittings, gas, offshore, waste gas, and pipelines
Properties of Graphite Sheet
SPECS	TEST METHOD	DATA
Carbon Content	-	98% min
Bulk Density	ASTM F1315	62.50 lbs/ft³ 1.00g/cm³
Ash Content	ASTM C561	<1%
Temperature	In oxidizing media	-400~842°F -240~450°C
Temperature	In non-oxidizing media	328~1598°F -200~870°C
Compressibility	ASTM F63A-66	40~50%
Recovery	ASTM F36A-66	10~15%
Creep Strength	At 7250 psi, 572°F 16hrs, DIN52913 At 50 N/mm² , 300°C 16hrs DIN52913	<6960 <45 N/mm²
Gas Permeability	DIN 3535, Thickness 0.06" DIN3535, Thickness 1.50mm	<0.41in³/s <0.40 cm³/min
Thickness of Reinforced Materials	-	0.2 mm 0.050 mm

Standard Sizes of Graphite Sheet

WIDTH x LENGTH	39.4" (+0.2")x39.4"(+0.2")	1000mm(+5mm) x 1000mm(+5mm)
	60.0"(+0.2") X 60.0"(+0.2")	1500mm(+5mm) x 1500mm(+5mm)
	39.4" (+0.2") x 80.0" (+0.2")	1000mm(+5mm) x 2000mm(+5mm)
THICKNESS	0.04"(±0.0032"),0.06 (±0.004") 0.08"(±0.0040"),0.12 (±0.004")	1.0mm(±0.08mm), 1.5(±0.10mm) 2.0mm(±0.10mm), 3.0(±0.10mm)

Package of Graphite Sheet

SIZE	PACKAGE
Thickness 0.04" (1.0mm) to 0.06" (1.5mm)	200 sheets in a vacuum sealed plastic bag, within a carton with a wooden crate
Thickness 0.08" (2.0mm) to 0.12" (3.0mm)	150 sheets in a vacuum sealed plastic bag, within a carton, with a wooden crate

Data are avarage results of test conducted under standard procedures and are subject to variation. Results should not be used for specification purposes.
Note: A material safety data sheet is available upon request.
The information, recommendations and opinions set forth herein are offered solely for your consideration, inquiry and verification, and are not, in part or total, to be construed as constituting a warrant or representation for which we assume legale responsibility. Nothing contained herein is to be interpreted as authorization to practice patented invention without a license.