E-Glass, Fiberglass Properties, InterSource USA, Inc.

Typical Data of E-Glass

Articles

Working Temp

Diameter (mm)

Texturized E-Glass fiber twisted rope
up 550° C

3,4,5,6,8,10,12,14,15,16,18,20,25,30,35,40

E-Glass Braided Packing

Articles	Working Temp	Diameter (mm)
Texturized E-Glass fiber round packing	up 550° C	5,6,8,10,12,14,15,16,18,20,25,30, 35,40,45,50

E-Glass Square Packing

The Main Application

Thermal insulation and sealing for various stove and boiler applications

Burner, chimney door sealing

Seal for heat exchanger, kiln car

Seal or insulation for heat registrant in furnace

Seal for high temperature valve or pump

Articles

Working Temp

Diameter (mm)

Texturized E-Glass fiber twisted square packing
up 550° C

5x5, 6x6, 8x8, 10x10, 12x12, 14x14, 15x15, 16x16, 18x18, 20x20, 25x25, 30x30, 35x35, 40x40, 45x45, 50x50

Technical of E-Glass Needlemat

E-Glass Fibers: are resistant to oils, solvents, and most chemicals although contact with hydrofluoric acids. Strong alkalis and live steam should be avoided.

are non combustible

have a low thermal conductivity

Color: White

Thermal Conductivity: Thermal 0.78 w/mK 300C mean

Loss on Ignition: <12%

Chemical of E-Glass Needlemat

E-Glass	SiO₂- 54.1%	Ai₂O₃- 15.3%
	CaO - 17.3%	MgO - 4.7%
	Na₂O - 0.6%	B₂O₃ - 8.0%

Availability of E-Glass Needlemat

Thickness
4mm

6mm

9mm

12mm

18mm

25mm

Weight per m² 150kg/m³
600

900

1350

1800

2700

3600

Weight per m² 130kg/m³
520

780

1171

1550

2340

3125

Roll Length
50

50

30

20

15

10

Density: available in a range of densities from 100-160 kg/m³
Width: 100cm standard (others available on request)

Typical Applications of E-glass Needlemat - Insulation media for exhaust silencers, Heatshields.

Data are average results of test conducted under standard procedures and are subject to variation. Results should not be used for specification purposes.
Note: A material safety data sheet is available upon request.
The information, recommendations and opinions set forth herein are offered solely for your consideration, inquiry and verification, and are not, in part or total, to be construed as constituting a warrant or representation for which we assume legal responsibility. Nothing contained herein is to be interpreted as authorization to practice patented invention without a license.